MATERIAL :

6061-T6 Aluminum Alloy: Silicon 0.4~0.8%, Copper 0.15~0.4%, Magnesium 0.8~1.2%, Chromium 0.404~0.35%, Ultimate Tensile Strength 290 MPa 42000 psi, Bearing Yield Strength 241 MPa 35000 psi, while thickness is less than0.25" (6.4mm)Tensile Strength is 8% or more. While thickness is greater than 0.25" (6.4mm), Tensile Strength is 10%.

SURFACE PROCESSING:

Anodized Color treatment: Corrosion resistant and 60 hours anti-UV endurance (tested under 100eV UV exposure for 60 hours before color starts fading, whereas natural UV radiation is around 3~10eV).

FEATURE:

The base is CNC machined from 6061 Aluminum and is T6 heat treated to offer better strength, hardness and flexibility than the average 6061. The impact shell is made from POM material which is high in tensile strength. The surface is anodized color treated finished with clear coating to preserve color vibrance under all weather conditions. The impact shell can be replaced to prolong usability.